TRA-BOND F112 adhesive is formulated for fiber optic assembly applications.
TYPICAL PROPERTIES OF UNCURED MATERIAL
Thixotropic Index 1.0
Viscosity @ 25 °C, mPa∙s (cP):
After Mixing 1,800
Specific Gravity, cured 1.2
Pot Life:
@ 2grams, minutes 30
Work Life:
@ 2grams, hour 1
Flash Point - See MSDS
TYPICAL CURING PERFORMANCE
Cure Schedule
24 hours @ 25°C or
1 hour @ 65°C or
15 minutes @ 90°C
Sufficient cure in 15 minutes @ 65oC is developed for polishing connectors.
The above cure profiles are guideline recommendations. Cure conditions (time and temperature) may vary based on customers' experience and their application requirements, as well as customer curing equipment, oven loading and actual oven temperatures.
TYPICAL PROPERTIES OF CURED MATERIAL
Physical Properties:
Coefficient of Thermal Expansion, cm/cm/oC 6.20×10+01
Glass Transition Temperature (Tg), ultimate, °C 102
Hardness, Shore D 86
Refractive Index 1.51
Water Absorption , after 24 hours saturation, % 0.07
tra-bond F112膠光纖裝配應(yīng)用制定。
固化材料的典型性能
觸變指數(shù)1
粘度@ 25°C，MPA∙S（CP）：
混合后的1800
比重，固化1.2
鍋里的生活：
“2grams，30分鐘
工作生活：
“2grams，小時(shí)1
閃光點(diǎn)看到MSDS
典型的固化性能
治療計(jì)劃
24小時(shí)@ 25°C或
1小時(shí)@ 65°C或
15分鐘@ 90°C
15分鐘@ 65oC足療用于拋光的連接器。
上述固化型材指南建議。固化條件（時(shí)間和溫度）可能會(huì)根據(jù)客戶(hù)的經(jīng)驗(yàn)和他們的應(yīng)用要求，以及客戶(hù)固化設(shè)備，烘箱負(fù)荷和實(shí)際烤箱溫度變化。
固化材料的典型性能
物理性質(zhì)：
熱膨脹系數(shù)，厘米/厘米/oC 6.20×10 + 01
玻璃化轉(zhuǎn)變溫度（Tg），極限，°C 102
硬度，岸上D 86
折射率1.51
吸水，24小時(shí)飽和度后，% 0.0 |
 |
|